Nomen mittentes508 Machina turpia
mittentes Pondus150Kg
Materia:QT450-10
Temperatus fundens:1420-1440℃
Opus Processus
Fac Core
Clausa arca
Clausa arca
Install poculum
Fundens
Fundens
Arca aperta
Arca aperta
Arca aperta
Repurgari fingunt
Repurgari fingunt
Repurgari fingunt
Frigus fingunt
Confer cum silica arena
2.1 Index comparationis testae lita arena
| Test Item | Silica harenae | Ceramic arena |
| Inflexio caloris vires （MPa） | 2.3 | 2.0 |
| Locus temperatus distrahentes vires （MPa） | 4.5 | 5.3 |
| Punctum liquescens | 96 | 96 |
| Gas evolutionis ml/g） | 15.2 | 12.1 |
| LOI（%） | 2.88 | 2.21 |
| Breathability（Pa） | 130 | 150 |
| Magnitudo (AFS) | 64.3 | 66.2 |
| High temperatus et pressura tempus S） | 83 | 98 |
| Mole Density（g/cm3） | 1.55 | 1.57 |
| linearibus expansionem rate % | 1.05 | 0.10 |
2.2 Comparatio proiectionis
Hsumma fortitudinis arenae silicae factae sunt 21 atrioli fusci, duo atri exigui flatura ob nucleum arenae fractum ac ferrum liquefactum acumen.,exiguo rate est 9.5%.Tota arena Ceramica facta est 14 atriculorum pede, faece nullo.
Scrap flatura
Singula
Virtus summus silica arena (p) ;Finis superficies pauperum fusorum et defectuum venarum in pariete interiore
Kaist arena Ceramic (t);Murus internus superficiei dejectionis est relative lenis, sine defectibus ut venae
Summus vires silica harenae
Kaist arena Ceramic
Kaist arena Ceramic
Summus vires silica harenae
Summus vires silica harenae
Summus vires silica harenae
Summus vires silica harenae
Summus vires silica harenae
Kaist arena Ceramic
conclusio
In Testa forma iactatus harenam eiectantem, compara cum altum robur harenae silicae, kaist Ceramic liquatur arena commoda altae fortitudinis, humilis gas evolutionis, aeris permeabilitas bona, longi temporis caliditas resistentiae, humilis expansio, etc., iactationes non abrasae sunt. superficies meta significantius emendatur, et venae defectus perfecte emendantur.